Title: | Cyclic Fatigue Behaviour of Wrought AZ80 Magnesium Alloy from Forged Automotive Wheel |
Authors: | Rivers, Geoffrey |
Advisor: | Niewczas, Marek |
Department: | Materials Science and Engineering |
Keywords: | Materials Science and Engineering;Materials Science and Engineering |
Publication Date: | 2011 |
Abstract: | <p>Wrought AZ80 magnesium alloy from a spoke of forged automotive wheel was subjected to high cycle fatigue to study its fatigue properties and to understand the relationship between the material substructure and fatigue life. The results reveal that in axial tension-compression S-N testing the spoke material exhibits an endurance limit of 98MPa and a sharp bend in the S-N curve. Fracture surface observation by SEM revealed rapid crack growth after crack nucleation with micro voids and angled secondary cracks throughout. XRD analysis revealed a strong material texture beneficial to basal slip activation before and after fatiguing, with small amounts of refinement after cycling and no signs of twinning. TEM observations of samples cycled at high stress and stresses above and below the endurance limit revealed a large difference in the dislocation substructures developed, which may relate to the sharp bend in the S-N curve.</p> |
URI: | http://hdl.handle.net/11375/9188 |
Identifier: | opendissertations/4333 5351 2040358 |
Appears in Collections: | Open Access Dissertations and Theses |
Files in This Item:
File | Size | Format | |
---|---|---|---|
fulltext.pdf | 21.96 MB | Adobe PDF | View/Open |
Items in MacSphere are protected by copyright, with all rights reserved, unless otherwise indicated.