Title: | Synthesis and Property Optimization of Ordered, Aryl Dense Polysiloxanes Using Boron Catalysis |
Authors: | Schneider, Alyssa F. |
Advisor: | Brook, Michael A. |
Department: | Chemistry and Chemical Biology |
Keywords: | Siloxanes;Piers-Rubinsztajn;Boron Catalysis;Aryl Silicones;Functional Elastomers;High-Throughput Synthesis;Hydrolysis |
Publication Date: | 2019 |
Abstract: | Silicones are widely used polymeric materials due to their unique properties. The material properties of silicones may be altered by incorporating various organic groups. Traditional methods for linear silicone synthesis involve ring-opening polymerization, which leaves the growing chain susceptible to acid or base mediated chain redistribution and the formation of cyclic monomer byproducts. The Piers-Rubinsztajn (PR) reaction is an alternative siloxane synthetic route that avoids the use of tin- or platinum- based, or of Brønsted acid/base catalysts. Siloxane bond formation is catalyzed by tris(pentafluorophenyl)borane (B(C6F5)3) (R’3Si-H + RO-SiR”3 → R’3Si-O-SiR”3 + RH); alkoxysilanes can be replaced with silanols or alkoxybenzenes. The catalytic activity of B(C6F5)3 was shown to be hindered by trace water in solution; water acts as a Lewis base coordinating to B(C6F5)3. Since the hydrate-free form of B(C6F5)3 is required to initiate a PR reaction, water can act as an inhibitor. In a somewhat contradictory fashion, water was also shown to react with hydrosilanes via a B(C6F5)3 catalyzed hydrolysis reaction to give silanols, that themselves are reagents for the process. The reactivity of alkoxysilanes (or aryl ethers) in the PR reaction was found to be much quicker than water. This was exploited in the synthesis of Ax(AB)yAx triblock copolymers. The aryl rich AB core was first synthesized using the PR reaction. Excess silicone condensed via hydrolysis forming the A blocks. This method of exploiting relative reactivity to tune structure was applied to elastomers made using a single linker (eugenol) with multiple functional groups – elastomer morphology was controlled by changing order of addition. The development of aryl dense silicones is of interest for use in electronic devices. Phenylmethyl homopolymers and highly ordered phenyl pendant copolymers (Ph/Si ratio of 0.5-1.5) were synthesized from monomers to give polymers with high refractive indices (1.51-1.59) and Mw up to 170 kDa. Statistically relevant libraries of aryl functional silicones were developed using combinatorial chemistry in order to analyze their structure-property relationship. Incorporating aromatic groups into silicones worked to elevate thermal stability, refractive index and improve the mechanical strength of silicone rubbers. |
URI: | http://hdl.handle.net/11375/24718 |
Appears in Collections: | Open Access Dissertations and Theses |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Schneider_Alyssa_F_2019July_PhDChemistry.pdf | 14.77 MB | Adobe PDF | View/Open |
Items in MacSphere are protected by copyright, with all rights reserved, unless otherwise indicated.